Abstract
Background/Aim: A newly-introduced tungsten containing rubber (TCR) is a potentially useful shielding material in electron radiotherapy because it is lead-free, containing as much as 90% fine tungsten powder by weight. This study aimed to investigate the shielding ability of TCR against electron beams. Materials and Methods: Transmission of TCR was measured for energies of 4, 6, 9 and 12 MeV. Dose profiles were measured to compare the TCR and lead. The electron backscatter factor (EBF) was also compared. Results: The transmission of equivalent thickness for 4, 6, 9 and 12 MeV with TCR (0.78%, 1.34%, 2.16% and 3.08%, respectively) were lower than that with lead (0.81%, 1.44%, 2.19% and 3.16%, respectively) (p<0.05). The dose profiles were not significantly different for TCR and lead. The EBF with TCR was up to 17% lower than that with lead. Conclusion: TCR has adequate radiation shielding ability for electron beams and could be employed instead of lead.
In electron radiotherapy, shields are placed on the patient's body surface or attached on the applicator to block beams and scattered rays. In general, the shielding is made from lead or a low-melting point alloy (LMA) and it limits radiation to the appropriate area by shaping the irradiation field. Lead and LMA provide excellent shielding against electron rays and are available at a reasonable price. There has been a number of reports on the dose characteristics of electron beams with lead shields and the dose is considered to depend on the energy, size of the irradiation field and thickness of the shielding material (1-4). However, lead shields are not easy to process, with odors during processing, harmful effects on the environment and possible toxicities for the human body (5). Materials made of high atomic-number elements, such as tungsten, are possible substitutes for lead (6, 7), although, they are costly and also difficult to process. Recently, easily processed tungsten functional paper (TFP) was described by Fujimoto et al., Monzen et al., Kamomae et al. and Tamura et al., who investigated its shielding abilities for x-rays, gamma rays and electron beams (8-11).
Tungsten containing rubber (TCR), a novel shielding material, was also recently developed. The aim of this study was to compare the shielding abilities of TCR and lead against electron beams. Their dosimetric characteristics with electron beams and their possible clinical applications were investigated.
Materials and Methods
Equipment. TCR was prepared by Hayakawa Rubber Co., Ltd. (Hiroshima, Japan) as a sheet-form shielding material, with a length and width of 25 cm, density of 7.65±0.03 g/cm3 and thickness and weight combinations of 1 mm for 0.5 kg and 2 mm for 1 kg (Table I shows other physical properties of TCR). The elemental ratios of TCR (mol%) were H: 1.0%, C: 6.5%, O: 0.5% and W: 90.0%. Electron beams with nominal energies of 4, 6, 9 and 12 MeV, generated by Synergy (Elekta, Stockholm, Sweden), were employed. The water-equivalent phantom, Tough Water Phantom (Kyoto Kagaku Co, Ltd., Kyoto, Japan) was used in this study. The following measurements were performed to evaluate the shielding ability of TCR: (1) The transmission for different TCR thicknesses, using a parallel-plate ionization chamber PPC40 (IBA Dosimetry GmbH, Germany); (2) The lateral dose profiles for the size of the irradiation field formed by processed TCR, using a 2D array detector Profiler2 (Sun Nuclear, FL, USA). The same measurements were also performed with a lead shield (Yoshizawa LD Co., Ltd., Osaka, Japan).
First, the equivalent thickness of shielding materials was set based on the maximum distance (Rmax) of each electron energy. Rmax is the largest penetration depth of electrons in the shielding. Therefore, the equivalent shield thickness was defined as the smallest integer that was larger than Rmax.
Rmax was calculated from the following formula (12): (1)
Table II shows Rmax and equivalent shield thicknesses of TCR and lead under the different electron energies.
Measurement of transmission and electron backscatter factor. The TCR and lead were separately placed on the surface of the water-equivalent phantom. The cone size was 10×10 cm2. The PPC40 was used in all measurements for point doses (13) (Figure 1A). At measurement, the monitor unit (MU) was set to 100 MU. First, the open field outputs without any shielding materials were measured at three reference points, which were at surface, 0.5 cm and 1.5 cm depths in the water-equivalent phantom. Second, the transmission of TCR with thicknesses of 1 to 12 mm was measured for electron energies of 4, 6, 9 and 12 MeV. Each transmission of the respective thickness was normalized by the open field output. In addition, transmission with TCR of equivalent thickness was also measured at a depth of the dose maximum (dmax) for each energy. The dmax values were 9 mm for 4 MeV, 13 mm for 6 MeV, 21 mm for 9 MeV and 28 mm for 12 MeV. Hence, the equivalent thicknesses of TCR and lead were 3 and 2 mm, respectively, for 4 MeV, 5 and 3 mm for 6 MeV, 7 and 5 mm for 9 MeV and 9 and 6 mm for 12 MeV. Finally, the electron backscatter factors (EBFs) for the equivalent thickness shielding materials were measured at depths ranging from 0 to 20 cm in the water-equivalent phantom, using PPC40 (Figure 1B). The electron backscatter contributes to producing significantly high dose enhancements near the tissue-shield interface. The enhancement in dose at the tissue–metal interface is dependent on the beam energy at the interface and the atomic number of the metal (13). The EBF was estimated by the following equation: (2)
Measurement of the dose profile. The geometry of the measurement of the dose profile is shown in Figure 1C. TCR was placed on the 2D array detector without any buildup materials (14). The TCR thicknesses were 3, 5, 7 and 9 mm for 4, 6, 9 and 12 MeV, respectively. The lateral dose profile was measured to evaluate the irradiation field size, the flatness and the penumbra trimmed by TCR. The evaluated irradiation field size was defined at the 50% dose level, which was normalized at the center. The flatness was calculated as the ratio of the maximum dose to the dose at the center of the field. The penumbra was determined as the distance between the 80% and the 20% dose points along the x-axis (13). The cone size was 10×10 cm2 and 3 cm in the positive direction of the x-axis was shielded. Therefore, the field negative direction of the x-axis was 5 cm and the positive direction of the x-axis was 2 cm opened, as shown in Figure 1C. For comparison, the lateral dose profile shielded by lead was measured under the same conditions. The thickness of the lead plate was based on information in Table II and the size of the irradiation field was also 2 cm.
Results
Measurement of transmission and electron backscatter factor. The result of measurements of TCR thickness and transmission for 10×10 cm2 field sizes at 4, 6, 9 and 12 MeV electron energies are shown in Figure 2 and Table III. The transmission was decreased exponentially, as the thickness of TCR was increased. At 4 MeV, 95% dose reduction was obtained with 2 mm TCR thickness. A 95% dose reduction was also obtained at 3 mm TCR thickness for 6 MeV, 5 mm for 9 MeV and 9 mm for 12 MeV. In addition, about a 20% dose increase because of build-up was observed with a shield thickness of 1 mm at electron energies of 9 and 12 MeV. The equivalent thickness of TCR was 3 mm for 4 MeV, 5 mm for 6 MeV, 7 mm for 9 MeV and 9 mm for 12 MeV. The equivalent thicknesses of TCR for each electron energy corresponded with most of the measurement results.
The transmission of 6 MeV for TCR thicknesses between 0 to 12 mm at measurement depths of surface, 0.5 cm and 1.5 cm is shown in Figure 3. The transmission was decreased exponentially as the thickness of TCR increased. The transmission of the equivalent shield thickness (5 mm) and the measured maximum shield thickness (12 mm) was 1.8% and 1.2% at surface, 1.6% and 1.0% at 0.5 cm, and 1.3% and 0.9% at 1.5 cm, which indicated that the differences were small. In addition, the increment of the surface dose was confirmed to be 1 mm TCR thickness, as shown in Figure 3. The results of transmission between TCR and lead with the equivalent shield thickness measured at dmax and with electron energies of 4 to 12 MeV are shown in Figure 4. With all electron energies from 4 to 12 MeV, the transmission of TCR was lower than that of lead and was lower by 0.1% at the maximum (p<0.05).
A comparison of EBF between TCR and lead at the corresponding equivalent shield thicknesses with electron energies of 4-12 MeV is shown in Figure 5. Each EBF was normalized by the respective measurement value of lead at a 0 cm depth. EBF with both TCR and lead decreased exponentially as the measurement depth increased. At all depths, the EBF of TCR was lower than that of lead, as well as at all electron energies. At a 0 cm depth and 4 MeV electron energy, the EBF of TCR was reduced by up to 17% compared with that of lead. The results of transmission for a 10×10 cm2 field size with 1 mm TCR thickness at electron energies of 4, 6, 9 and 12 MeV are shown in Figure 6. Each transmission curve was normalized by the measurement value without TCR for dmax corresponding to each electron energy. With electron energies of 4 and 6 MeV, as measurement depth was greater, the transmission with 1 mm TCR thickness was decreased exponentially. With electron energies of 9 and 12 MeV, as measurement depth increased, the transmission with 1-mm TCR thickness showed a shouldering exponential decline. As electron energy increased, the dose increment was 0 cm. The results of the transmission at 0 cm were: 57.98% for 4 MeV, 99.13% for 6 MeV, 120.84% for 9 MeV and 121.59% for 12 MeV.
Measurement of dose profile. The lateral dose profiles with TCR and lead at 4, 6, 9 and 12 MeV electron energies are shown in Figure 7. As the energy of the electron beam increased, the dose of the periphery of the shield edge was increased for both TCR and lead. Table IV shows the results of the covered side of the field size, flatness and penumbra of TCR and lead for each electron energy. The results of the covered side of the field size of TCR and lead under the respective energies were 2.08 and 2.04 cm for 4 MeV, 2.09 and 2.08 cm for 6 MeV, 2.09 and 2.12 cm for 9 MeV, 2.13 and 2.10 cm for 12 MeV. The results of the covered side of the flatness of TCR and lead under the respective energies were 100.29% and 100.23% for 4 MeV, 100.59% and 100.54% for 6 MeV, 102.42% and 102.19% for 9 MeV, 102.53% and 103.59% for 12 MeV. The results of the covered side of the penumbra of TCR and lead were 0.68 and 0.69 cm for 4 MeV, 0.60 and 0.60 cm for 6 MeV, 0.53 and 0.51 cm for 9 MeV and 0.49 and 0.52 cm for 12 MeV. These results showed that the dose profiles were not significantly different for TCR and lead.
Discussion
In this study, the shielding abilities of TCR and lead were compared to clarify the dosimetric characteristics of TCR for electron beams and, therefore, its potential use in clinical applications.
Transmission was decreased with increased TCR thickness. However, increased transmission was observed when TCR thickness was 1 mm for electron beams of greater than 9 MeV, because buildup occurred at a depth of 0.5 cm. These findings correlated well with previous studies. For the equivalent TCR shield thickness, transmission was attenuated more than 95% for each energy, as shown in Figure 2. This was enough to shield the electron beams in a manner similar to shielding by lead (Figure 4). In electron-beam therapy of up to 12 MeV, TCR with a 9 mm thickness could be used sufficiently at clinical sites without any shielding concerns. In addition, the equivalent shield thickness calculated from Rmax was confirmed to be a useful index for calculating the equivalent TCR thickness for a clinical site.
Fujimoto et al. showed that the irradiation field size was nearly equal for TFP and lead. However, the lateral dose profile of the irradiation field shaped with TFP gradually increased in dose toward the periphery of the irradiation field. Our results agreed well with this report. As with TFP, TCR and lead had similar dose characteristics against electron beams (8). In the lateral dose profiles, the irradiation field size, flatness and penumbra for TCR were nearly equal to those for lead. The difference between the peripheral and the central dose was the largest at an electron energy of 12 MeV, 2.5% for TCR and 3.6% for lead. The increase in peripheral dose was caused by scattered rays from the shielding material and depended primarily on shield thickness.
TFP and a hydrogenated styrene-butadiene-styrene copolymer (SEBS) described by Yue et al. were also studied as new shielding materials for electron radiotherapy (6, 8, 11). TCR has useful characteristics similar to those of TFP and SEBS. First, TCR is softer and easier to process than lead. TCR is expected to shape irradiation fields that are equivalent to or even more complicated than those shaped by other materials. Conventional electron radiotherapy was performed with the tubus, collimator or shield made from lead or LMA. The irradiation field of the tubus was limited to a predetermined aperture size and a collimator and shield made from lead or LMA required a long time to shape the irradiation field. However, TCR can shape an irradiation field more flexibly and quickly than these other materials. Second, TCR can also be used for grid therapy, instead of TFP (11). It is possible to restore the penumbra when treating at extended SSD by placing collimation on the skin surface (13). When placed on patients, TCR can suppress their movement. In addition, TCR is soft enough to be placed on a curved part of a patient's body, such as the face, ear, shoulder or belly. Meanwhile in the clinic, the bremsstrahlung caused by interactions between the electron beam and the shield, and the bolus effects of the shield itself are potential problems (8, 11, 15). Generally, bremsstrahlung is proportional to the electron energy and the atomic number of the shielding material. Tungsten may reduce bremsstrahlung, compared with lead, because of its lower atomic number. If the shielding materials are placed directly on the patient's skin surface, a bolus effect could result (8). However, the bolus effect from TCR was smaller than that from lead. As Figure 5 shows, TCR could reduce the skin surface dose up to 17%, compared with lead, when placed directly on the patient's skin surface. One reason for this might be because TCR is a mixture of high and low density materials (16). Conversely, the bolus effect caused by 1 mm thick TCR, as shown in Figure 7, suggested that it has advantages for radiation therapy on the skin surface, such as in treating angiosarcoma.
TCR can readily shape the irradiation field and is less harmful to the human body than LMA, which releases toxic substances during processing, although at levels lower than the reference (5). While the cost of TCR is slightly higher than that of lead of the same size, the price may be reduced by recycling or re-manufacturing after use and, in addition, we are developing a non-disposable clay-like TCR. This could make it possible to use limited resources effectively in the future.
Conclusion
TCR is a novel and flexible shielding material containing a metal with a high atomic number in rubber and it has a shielding ability that is equivalent to or higher than that of lead. TCR has adequate radiation shielding ability for electrons within the energy range used in radiotherapy and could, therefore, be employed instead of lead at clinical sites.
Acknowledgements
This work was supported partly by JSPS KAKENHI grant numbers 16K09027 and 17K09071. The Authors thank Susan R. Doctrow, PhD, from Edanz Group (www.edanzediting.com/ac) for editing a draft of this manuscript.
Footnotes
Conflicts of Interest
Hajime Monzen received a research donation from Hayakawa rubber Co., LTD.
- Received April 20, 2018.
- Revision received May 21, 2018.
- Accepted May 23, 2018.
- Copyright© 2018, International Institute of Anticancer Research (Dr. George J. Delinasios), All rights reserved